Kinkou-96 Copper Unloy (Cu-9ni-6sn C72700)
1. Vailaau o le C72700
| Faʻataʻitaʻiga | Ni | Sn | Mn | Pb | Zn | Fe | P | Afaina | Cu |
| C72700 | 8.5-9.5 | 5.5-6.5 | 0.05-0-.3 | ≤0.03 | ≤0.15 | ≤0.05 | ≤0.05 | ≤0.5 | Toega |
2. Tulaga tino o le C72700
| Tulaga | 8.9 | (g / cm3) |
| Liusuavai manatu | 968-1078 | (℃) |
| Le lelei le maualuga | 17.25 | (X10-6/ ℃) 20-200 ℃ |
| Elerad Modulus | 120 | (GPA) |
| Eletise eletise i le 20 ℃ |
| μω * cm |
| Quanch | ≤19.5 |
|
| Faaosofia le malosi | ≤15 |
|
| Eletise eletise (iscs,%) |
| (% ICS) |
| ≥9 |
| |
| O le faatupu vevesi e puipuia (3 itula) | ≥12 |
|
| Teraional Modulus | 50 | (GPA) |
| O le le togafitia o le Faletupe i le 20 ℃ | 53.6 | (W / mk) |
| Punou le mafaufau vaivai | 450 | (Mpa) |
3. Masini masini / setete o C72700
1) Reart oloa
| Setete | Maamatami | Malosi le malosi | Fuatia malosi | Elongaon | Punou * | Le malosi, manaia ma punou palu anufe (mpa) | ||
| HV | Rm (mpa) | RP 0.2 (MPA) | A50mm (%) | Laumua // | Liua | Laumua // | Liua | |
| Quanching | ||||||||
| TB | 90-125 | 420-500 | ≥200 | ≥30 | 0.2 | 0.2 | 302 | 220 |
| Quanching / malulu roling | ||||||||
| TD1 | 140-180 | 460-560 | ≥300 | ≥15 | 0.2 | 0.2 | 216 | 359 |
| Td2 | 160-200 | 540-640 | ≥400 | ≥10 | 0.2 | 0.2 | 275 | 390 |
| TD3 | 200-240 | 620-720 | ≥550 | ≥3 | 0.5 | 0.5 | 444 | 523 |
| TD4 | 220-260 | 700-820 | ≥600 | ≈1 | 2 | 1 | 467 | 568 |
| Tdx | ≤320 | ≥780 | ≥650 | ≈1 | 10 | 2 | 472 | 613 |
| Faʻaiuga / Faʻaiuga vevela togafitiga | ||||||||
| TF | 230-270 | 740-860 | ≥510 | ≥10 | 0.5 | 0.5 | 566 | 634 |
| Quanching / malulu rolling / timuga vevela togafitiga | ||||||||
| Th1 | 4.0-310 | 850-950 | ≥650 | ≥8 | 0.5 | 0.5 | 684 | 724 |
| Th2 | 290-320 | 880-980 | ≥720 | ≥8 | 1 | 1 | 730 | 770 |
| Th3 | 310-340 | 950-1050 | ≥800 | ≥4 | 1 | 1 | 829 | ≥840 |
| O4 | 320-360 | 1000-1100 | ≥900 | ≈3 | 2 | 2 | ≥830 | ≥840 |
| Faafetai | ≤390 | ≥1050 | ≥950 | ≈1 | / | / | ≥830 | ≥840 |
| *: E tusa ai ma Disco111 (25/10/85), punou 90 ° i le tulaga faʻataʻitaʻi, vaevae le itiiti ifo i le mafiafia e iloa ai le mea mafiafia | ||||||||
2) oloa tusia
| Setete | Maamatami | Malosi le malosi | Fuatia malosi | Elongaon | Faalauteleina lelei |
| HV | Rm (mpa) | RP 0.2 (MPA) | A50mm (%) | Z% | |
| Quanching | |||||
| TB | ≤150 | 400-500 | ≥200 | ≥30 | ≥80 |
| Quanching / malulu roling | |||||
| TD1 | 150-180 | 500-580 | ≥300 | ≥10 | ≥75 |
| Td2 | 180-230 | 550-720 | ≥500 | ≥3 | ≥70 |
| TD3 | 220-260 | 700-800 | ≥600 | ≥2 | ≥65 |
| TD4 | 230-300 | 780-880 | ≥700 | ≥1.5 | ≥60 |
| Tdx | 250-320 | 880-1000 | ≥800 | ≥0.1 | ≥50 |
|
|
|
|
|
|
|
| Setete | HV | Rm (mpa) | RP 0.2 (MPA) | A50mm (%) | Z% |
| Faʻaiuga / Faʻaiuga vevela togafitiga | |||||
| TF | ≤260 | 770-870 | ≥500 | ≥20 | ≥40 |
| Quanching / malulu rolling / timuga vevela togafitiga | |||||
| Th1 | 260-300 | 8700-970 | ≥700 | ≥13 | ≥30 |
| Th2 | 290-310 | 930-1030 | ≥800 | ≥8 | ≥30 |
| Th3 | 310-330 | 1000-1100 | ≥900 | ≥5 | ≥30 |
| O4 | 330-360 | 1100-1200 | ≥1000 | ≥2 | ≥30 |
| Faafetai | ≥350 | 1175-1300 | ≥1100 | ≥0.5 | ≥30 |
4. Tapulaa le faapalepale o le rod ma uaea o c72700
| Ituaiga | Lapoa | Faapalepale o le lautele | Faapalepale o le sao | |||
| inisi | mm | inisi | mm | inisi | mm | |
| Uaea | 0.2-.39 | 6.35-9.9 | +/- 0. 0.002 | +/- 0.05 | Umi = 10ft, devigation <0.25 inisi | umi = 3048mm, devigation <6.35mm |
| 0.4-0.74 | 10-18.9 | + 0.005 / -0 | + 0.13 / -0 | |||
| Tootoo | 0.75-1.6 | 19-40.9 | + 0.02 / + 0.08 | + 0.5 / + 2.0 | Umi = 10ft, deving <0.5 inisi | umi = 3048mm, devigation <12mm |
| 1.61-2.75 | 41-70 | + 0.02 / + 0.10 | + 0.02 / + 0.10 | |||
| 2.76-3.25 | 70.1-82 | + 0.02 / + 0.145 | + 0.02 / + 0.145 | |||
| 3.26-6.00 | 83-152.4 | + 0.02 / + 0.187 | + 0.02 / + 0.187 | |||
| <0.4 | <10 | +/- 0. 0.002 | +/- 0.05 |
|
| |